K. Zielińska; M. Włoczewski; R. Psiuk; J. Hoffman; E. Wojtiuk; P. Bazarnik; T. Mościcki
Ceramics International 52 (2026) 31867–31882
Transition metal borides are attracting increasing interest due to their unique properties. They are not only characterised by very high hardness, but also considerable chemical and thermal stability. Silver, on the other hand, is a good material for increasing electrical and thermal conductivity, wear resistance and has antibacterial properties due to its biological characteristics. Combining these two materials can provide superhard bilayers with increased functional properties. In this study, it was decided to synthesise Ag/WB2.5, Ag/W0.76Ti0.24B2.5 coatings and compare their properties to the individual components. The silver coating was produced by pulsed laser deposition (PLD), while the WB2.5 and W0.76Ti0.24B2.5 coatings were formed by high-power pulsed magnetron sputtering (HiPIMS). To determine the mechanical properties, nanoindentation tests, adhesion of the coatings by scratch -test and wear resistance by abrasion in reciprocating motion were tested. In all cases, the silver film contributed to an increase in the wear resistance of the materials without major changes in the hardness results of the materials. In addition, the Ag/W0.76Ti0.24B2.5 film showed very good adhesion to the substrate. Human hand wiping simulator was also carried out using – Tribotouch. After 36 000 cycles Ag/W0.76Ti0.24B2.5 coating was slightly deformed, which was not visible macroscopically. This result is more than three times greater than for the pure silver film. It was also decided to carry out corrosion tests in an environment of 0.9% NaCl. The Ag/W0.76Ti0.24B2.5 bilayer has very good corrosion resistance, similar to pure silver.